Hardness of Lead Alloys

[fd-ems-emt]

For all of you caster out  there..
Here is table of Hardness of Lead Alloys



Alloy                      % Lead        % Tin         % Antimony         BHN Hardness

Monotype                    72               9                 19                         28

Stereotype                  80               6                 14                         23

Linotype                      84               4                 12                         22

Lyman #2                    90               5                 5                           15

Taracorp Magnum          92               2                 6                           15

1:1 Lead/Lino                92               2                 6                           15

Electrotype                  94.5            3                 25                         12

10:1                             91               9                 0                           11.5

16:1                             94               6                  0                          11

20:1                             95               5                  0                          10

30:1                             97               3                  0                            9

40:1                             97.5            2.5                0                           8.5

Wheel-weight                95               0.5                4                           9

Pure Lead                      100              0                  0                           5

[Bountyhunter]

Lots of folks test their lead by the fingernail test.  If they can scratch it with a fingernail, it is considered by some to be soft.

In the BHN hardness, an average persons fingernail is about 13 bnh.  A person who is used to hard labor, or shopwork may be 14 or 15.

The fingernail test tells you that the hardness of the lead is less than the hardness of the fingernail, nothing more.  It is more softer than more harder.   So lead that can be scratched with the fingernail is usually less than 13 BNH.

[Hawg Haggen]

On the wheel weights you only have the clip on weights listed. Stick on weights are 99.5% pure lead with a BHN of six. Plenty soft enough for round balls, conicals and minies. Here is a more indepth article on bullet casting alloys. http://www.lasc.us/CastBulletAlloy.htm

Common Bullet Alloys,
Composition and Hardness

Alloy    Tin%    Antimony%    Lead%    BHN    Arsenic
(Trace)
Foundry Type    15    23    62    ?    No
Monotype    9    19    72    28    No
Stereotype    6    14    80    23    No
Linotype    4    12    80    23    No
Lyman # 2    5    5    90    15    No
Electrotype    3    2.5    94.5    12    No
1 to 10 tin/lead    9    ---    91    11.5    No
1 to 20 tin/lead    5    ---    95    10    No
1 to 30 tin/lead    3    ---    97    8    No
1 to 40 tin/lead    2.5    ---    97.5    6-7    No
Hard Ball    2    6    92    16    No
Clip-on    .5    3-4    95.5    10    Yes
wheel weight    96.5    12
Stick-on    *    **    99.5    6    No
wheel weight
# 8 Magnum    ---    2-3%    97-98    ***    Yes
Plumbers Lead    ---    ---    ****100        No
Lead    ---    ---    100    5    No